3748 VO-TC 3M, 3748 VO-TC Datasheet - Page 2
![HOT MELT ADHESIVE VO 5/8"X2"](/photos/15/53/155352/3748_vo-tc_sml.jpg)
3748 VO-TC
Manufacturer Part Number
3748 VO-TC
Description
HOT MELT ADHESIVE VO 5/8"X2"
Manufacturer
3M
Series
Scotch-Weld™r
Type
Adhesive Cartridger
Specifications of 3748 VO-TC
Features
Non-Corrosive
For Use With/related Products
Ceramic, Glass, Polyolefin
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Other names
0 00 21200 85816 1
3M6416
62376898300
3M6416
62376898300
3M
Self-Extinguishing Hot Melt Adhesive
3748 VO
Typical Performance
Properties
™
Scotch-Weld
Note: The following technical information and data should be considered representative
(1) 1" x 4" Douglas Fir specimens are bonded with hot melt adhesive using a 1" overlap shear
(2) 1" x 4" Douglas Fir specimens are bonded with hot melt adhesive using a 1" overlap and 13 mil wire
(3) Test involves bonding .020" wire mesh (galvanized window screen type) to substrate using hot melt
Two Pound Dead Load Heat Resistance
(3M TM C 3093)
Overlap Shear Strength @ 70°F (21°C)
(3M TM C 3096)
180° Peel Adhesion
(3M TM C 3168)
Wire Mesh to FR-4
Weight Loss by TMA (In Air)
Thermal Coefficient of Expansion by TMA
Thermal Conductivity (@ 41°C [107°F] on .020" samples)
Thermal Shock Resistance
configuration. Bonds are then conditioned for 24 hours at 70°F (22°C), 50% relative humidity before
testing. Bonds are subjected to 2 lbs. per square inch load at 100°F (49°C) for 30 minutes.
Temperature of the bond line is raised every 30 minutes until failure. Heat resistance recorded is the
last temperature prior to bond failure.
spacer to set bond line thickness. Bonds are then conditioned for 24 hours at 70°F (22°C), 50%
relative humidity before testing. Bonds are pulled in shear at a separation bond speed of 2 inch a
minute recording strength at failure.
adhesive. Wire mesh is encapsulated with adhesive. After conditioning, bond is tested by 180° peel
back method using Instron at 10 inches per minute peel speed.
™
or typical only and should not be used for specification purposes.
Over -100 to -40°C temperature range
BTU-ft./ft
FR-4 to FR-4
Fir to Fir
Polypropylene to Polypropylene
Polyethylene to Polyethylene
Temperature of weight loss at 5°C/min
Over -20 to 25°C temperature range
Cal./sec. - cm - °C
Watt/m - °C
J/cm - sec - °C
Potted Washer Olyphant test
(3M TM C3167)
+ 100°C (air) to -40°C (liquid)
to PP
to PE
to Fir
2
-hr. - °F
(1)
(2)
(1)
- 2 -
154.5 x 10
-34.0 x 10
10% @ 673°F (356°C)
1% @ 459°F (237°C)
5% @ 621°F (327°C)
Passes 5 cycles
175°F (79°C)
w/o cracking
1.11 x 10
4.58 x 10
1.92 x 10
1.92 x 10
215 psi
275 psi
250 psi
220 psi
38 piw
35 piw
27 piw
26 piw
-6
-6
units/units/°C
units/units/°C
-1
-4
-1
-3