5519 1.0MM 3M, 5519 1.0MM Datasheet - Page 2

• Manufacturer Part Number: 5519 1.0MM
• Description: THERMALLY CONDUCTIVE INTERFACE PAD
• Manufacturer: 3M

Specifications of 5519 1.0MM

• Thermal Conductivity: 4.9W/m.K

Aged at 130°C in high temperature chamber.
Note: Thermal Conductivity for aging tested using the QTM-500 Hot Wire Test Method. Values can differ from an ASTM-D5470 TM due to TM differences.
3M
Typical Physical Properties
Note: The following technical information and data should be considered representative or typical only and should not be
Notes:
1) Shore OO Test Method based on a 6mm thick sample. Results will vary for different thickness samples.
2) Thermal conductivity can vary with test method and/or equipment used for testing at different test sites.
Compression vs. Stress
Environmental Aging Data
Heat resistance of 1.0 mm 3M™ Hyper Soft Thermally Conductive Interface Pad 5519
100%
80%
60%
40%
20%
™
0%
used for specification purposes.
Property
Thermal Conductivity (W/mK)
Flammability
Density (g/cm
Hardness
Volume Resistivity (Ω-cm)
Dielectric Strength (kV/mm)
Dielectric Constant
Hyper Soft Thermally Conductive Interface Pads 5519 and 5519S
Duration (hrs)
Thermal Conductivity (W/mK)
Hardness (Shore 00)
Appearance
0
3M™ Hyper Soft Thermally Conductive
Interface Pad 5519 (1 mm)
Rate: 0.5 mm/min
3
, @ 25°C)
1
Note 2
2
Stress (MPa)
Initial
4.9
69
–
3M™ Hyper Soft Thermally Conductive Interface Pads 5519 and 5519S
3
ASTM D5470
Shore 00
ASTM D257
ASTM D149
ASTM D150
Method
UL 94
(2)
–
Note 1
No effect
500
4.9
70
4
5
No effect
1000
4.9
70
19.5 (1-100 kHz)
5519 @ 70
5519S @ 75
1.7 x 10
Value
4.9
3.1
1.1
V0
14
No effect
3000
4.9
70