507-1446 MULTICOMP, 507-1446 Datasheet - Page 2
![no-image](/images/manufacturer_photos/0/4/462/multicomp_sml.jpg)
507-1446
Manufacturer Part Number
507-1446
Description
SOLDER WIRE, , 1.2MM, 500G
Manufacturer
MULTICOMP
Datasheet
1.507-1380.pdf
(3 pages)
Specifications of 507-1446
External Diameter
1.2mm
Material Composition
99.3% Tin, 0.7% Copper
Melting Temperature
227°C
Weight
0.5kg
Svhc
No SVHC (18-Jun-2010)
Bit Temperature
350°C
Flux Type
400, Rosin Based, Halide Free
Wire Diameter
1.2
Rohs Compliant
Yes
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Flux: The solid fluxes are based on modified rosins and carefully selected activators. In use they exhibit a mild rosin odour and leave
a small quantity of clear residue.
Cored wire: Multicomp Typ 400, 505 & 511 cored solder wires are designed to give fast and sustained wetting on both copper and
brass. This can be demonstrated using spreading tests on both substrates under standard conditions for the Multicomp products and
comparable competitor products. After 5 seconds, area of spread is measured to form a comparative index indicating total flux
efficacy.
Multicomp Typ 400, 505 & 511 flux cored solder wires out-perform competitor products, which required a higher flux content and
leave more residues whilst achieving poorer spread.
* Oxidised for 1 Hour at 205°C.
* Oxidised for 1 Hour at 205°C.
Acid Value mg/KOH/g
Halide Content %
J-STD-004
-Solder Spread mm
-Corrosion Test
SIR Test (Without Cleaning)
-IPC-SF-818 Class3
-Bellcore TR-NWT-000078
Elektromigration-Test SIR Test (Without Cleaning) Bellcore TR-NWT-000078
Classification
-EN 29454-1
-J-STD-004
-IPC-SF-818
Type 400
Competitor A
Competitor B
Competitor E
Competitor F
Competitor G
Competitor H
Type 505
Solder Wire
Lead F F ree
http://www.farnell.com
http://www.newark.com
http://www.cpc.co.uk
Product
Product
Relative Wetting Performance of Multicomp Solder Wire and Halide Free Competitor Products *
Relative Wetting Performance of Multicomp Solder Wire and Halide Free Competitor Products *
2
Flux Content
Test
2.0
2.4
3.5
2.7
3.0
%
Flux Content
2.2
3.5
%
Kristall Flux Properties
Halide Content
Page <2>
0.4
0.5
%
Area of Spread, mm
Oxidised Copper
222
191
202
Oxidised Copper
LR3CN
RO L0
Pass
Pass
1.2.3
400
215
210
0
200
190
150
230
220
2
Area of Spread, mm
MR3CN
RO M1
Pass
Pass
1.2.2
505
170
315
0,5
Oxidised Brass
Oxidised Brass
209
140
09/03/09 V1.1
2
150
180
120
150
240
MR3CN
RO M1
Pass
Pass
1.2.2
511
170
340
1,1