41104 Loctite, 41104 Datasheet

ETHYL CYANOACRYLATE ADH, TUBE, 3G

41104

Manufacturer Part Number
41104
Description
ETHYL CYANOACRYLATE ADH, TUBE, 3G
Manufacturer
Loctite
Series
411r
Datasheet

Specifications of 41104

Adhesive Type
Ethyl Cyanoacrylate
Adhesive Applications
Gap Filling / Bonding
Color
Clear
Dispensing Method
Tube
Weight
3g
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
PRODUCT DESCRIPTION
LOCTITE
characteristics:
LOCTITE
suitable for bonding rubber, plastic and metals. LOCTITE
411™ exhibits excellent peel strength and added heat
resistance.
TYPICAL PROPERTIES OF UNCURED MATERIAL
TYPICAL CURING PERFORMANCE
Under normal conditions, the atmospheric moisture initiates the
curing process. Although full functional strength is developed
in a relatively short time, curing continues for at least 24 hours
before full chemical/solvent resistance is developed.
Cure Speed vs. Substrate
Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. Thin bond
lines result in high cure speeds, increasing the bond gap will
decrease the rate of cure.
Cure Speed vs. Activator
Where cure speed is unacceptably long due to large gaps,
applying activator to the surface will improve cure speed.
However, this can reduce ultimate strength of the bond and
therefore testing is recommended to confirm effect.
Technology
Chemical Type
Appearance (uncured)
Components
Viscosity
Cure
Application
Key Substrates
The rate of cure will depend on the substrate used. The table
below shows the fixture time achieved on different materials
at 22 °C / 50 % relative humidity. This is defined as the time to
develop a shear strength of 0.1 N/mm².
Specific Gravity @ 25 °C
Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):
Flash Point - See MSDS
Fixture Time, seconds:
Spindle TC, speed 20 rpm, Helipath
Steel (degreased)
Aluminum
Neoprene
Rubber, nitrile
ABS
PVC
Polycarbonate
Phenolic
®
®
411™ is a general purpose gap filling adhesive
411™
provides
Cyanoacrylate
Ethyl cyanoacrylate
Water white to slightly cloudy gel
One part - requires no mixing
High
Humidity
Bonding
Rubbers, Plastics and Metals
the
following
4,000 to 8,000
1.05
20 to 50
10 to 30
<5
<5
15 to 40
20 to 50
30 to 70
10 to 40
product
LMS
LMS
®
TYPICAL PROPERTIES OF CURED MATERIAL
TYPICAL PERFORMANCE OF CURED MATERIAL
Cured for 24 hours @ 22 °C
Adhesive Properties
Cured for 30 seconds @ 22 °C
Cured for 24 hours @ 22 °C
Cured for 24 hours @ 22 °C, followed by 24 hours @ 121 °C, tested
@ 121 °C
Physical Properties:
Electrical Properties:
Tensile Strength, ISO 6922:
Lap Shear Strength, ISO 4587:
Tensile Strength, ISO 6922:
Lap Shear Strength, ISO 4587:
Coefficient of Thermal Expansion,
Coefficient of Thermal Conductivity, ISO 8302,
W/(m·K)
Glass Transition Temperature, ASTM E 228, °C 120
Dielectric Constant / Dissipation Factor, IEC 60250:
Volume Resistivity, IEC 60093, Ω·cm
Dielectric Breakdown Strength,
IEC 60243-1, kV/mm
Buna-N
Steel (grit blasted)
Aluminum (etched)
ABS
PVC
Polycarbonate
Phenolic
Neoprene
Nitrile
Steel (grit blasted)
Steel (grit
ISO 11359-2, K
0.05-kHz
1-kHz
1,000-kHz
LOCTITE
-1
blasted)
N/mm² ≥7.0
(psi)
N/mm² 18 to 26
(psi)
N/mm² 11 to 19
(psi)
N/mm² >6
(psi)
N/mm² >6
(psi)
N/mm² >5
(psi)
N/mm² 5 to 15
(psi)
N/mm² >10
(psi)
N/mm² >10
(psi)
N/mm² 12 to 25
(psi)
N/mm² ≥8.3
Technical Data Sheet
®
September-2009
(≥1,015)
(2,610 to 3,770)
(1,595 to 2,755)
(>870)
(>870)
(>725)
(725 to 2,175)
(>1,450)
(>1,450)
(1,740 to 3,625)
411™
80×10
0.1
10×10
25
2.3 / <0.02
2.3 / <0.02
2.3 / <0.02
LMS
LMS
-6
15

41104 Summary of contents

Page 1

... Key Substrates Rubbers, Plastics and Metals ® LOCTITE 411™ general purpose gap filling adhesive suitable for bonding rubber, plastic and metals. LOCTITE 411™ exhibits excellent peel strength and added heat resistance. TYPICAL PROPERTIES OF UNCURED MATERIAL Specific Gravity @ 25 °C Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP): ...

Page 2

... For best performance bond surfaces should be clean and free from grease. 2. This product performs best in thin bond gaps (0.05 mm). 3. Excess adhesive can be dissolved with Loctite cleanup solvents, nitromethane or acetone. Loctite Material Specification LMS dated November-21, 2002. Test reports for each batch are available for the indicated properties ...

Page 3

... U.S. Patent and Trademark Office. Reference 2.2 Henkel Americas +860.571.5100 For the most direct access to local sales and technical support visit: www.henkel.com/industrial We cannot assume Henkel Europe +49.89.320800.1800 ® TDS LOCTITE 411™, September-2009 Henkel Asia Pacific +86.21.2891.8863 ...