45440 Loctite, 45440 Datasheet

ETHYL CYANOACRYLATE ADH, TUBE, 20G

45440

Manufacturer Part Number
45440
Description
ETHYL CYANOACRYLATE ADH, TUBE, 20G
Manufacturer
Loctite
Series
454r
Datasheet
1.45440.pdf (2 pages)

Specifications of 45440

Adhesive Type
Ethyl Cyanoacrylate
Adhesive Applications
Bonding - General Purpose
Color
Clear
Dispensing Method
Tube
Weight
20g
Pack Quantity
1
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
PRODUCT DESCRIPTION
LOCTITE
following product characteristics:
LOCTITE
the rapid bonding of a wide range of materials, including
metals,
Instant Adhesive Gel is particularly suited for bonding porous
or absorbent materials such as wood, paper, leather and fabric.
The gel consistency prevents adhesive flow even on vertical
surfaces.
TYPICAL PROPERTIES OF UNCURED MATERIAL
TYPICAL CURING PERFORMANCE
Under normal conditions, the atmospheric moisture initiates the
curing process. Although full functional strength is developed
in a relatively short time, curing continues for at least 24 hours
before full chemical/solvent resistance is developed.
Cure Speed vs. Substrate
Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. Thin bond
lines result in high cure speeds, increasing the bond gap will
decrease the rate of cure.
Technology
Chemical Type
Appearance (uncured)
Components
Viscosity
Cure
Application
Key Substrates
The rate of cure will depend on the substrate used. The table
below shows the fixture time achieved on different materials
at 22 °C / 50 % relative humidity. This is defined as the time to
develop a shear strength of 0.1 N/mm².
Specific Gravity @ 25 °C
Flash Point - See MSDS
Casson Viscosity, 25 °C, mPa·s (cP):
Fixture Time, ISO 4587, seconds:
Cone and plate rheometer
Steel (grit blasted)
Neoprene
PVC
Paper
®
®
plastics and
Quicktite
Quicktite
®
®
Instant Adhesive Gel is designed for
Instant Adhesive Gel provides the
Cyanoacrylate
Ethyl cyanoacrylate
Transparent, colorless gel
One part - requires no mixing
Gel
Humidity
Bonding
Wood, Paper, Leather and Fabric
elastomers. LOCTITE
1.1
100 to 450
30
60
15
≤30
®
LMS
LMS
Quicktite
LMS
®
Cure Speed vs. Humidity
The rate of cure will depend on the ambient relative humidity.
Higher relative humidity levels result in more rapid speed of
cure.
Cure Speed vs. Activator
Where cure speed is unacceptably long due to large gaps,
applying activator to the surface will improve cure speed.
However, this can reduce ultimate strength of the bond and
therefore testing is recommended to confirm effect.
TYPICAL PERFORMANCE OF CURED MATERIAL
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Material Safety Data Sheet (MSDS).
Directions for use
Loctite Material Specification
LMS dated March-19, 2002. Test reports for each batch are
available for the indicated properties. LMS test reports include
selected QC test parameters considered appropriate to
specifications for customer use. Additionally, comprehensive
controls are in place to assure product quality and
consistency. Special customer specification requirements may
be coordinated through Henkel Quality.
Adhesive Properties
Cured for 24 hours @ 22 °C
LOCTITE
1. For best performance bond surfaces should be clean and
2. This product performs best in thin bond gaps (0.05 mm).
3. Excess adhesive can be dissolved with Loctite cleanup
Block Shear Strength, ISO 13445:
Lap Shear Strength, ISO 4587:
Instant Adhesive Gel
PVC
Steel (grit blasted)
Neoprene
free from grease.
solvents, nitromethane or acetone.
* substrate failure
®
LMS
Quicktite
N/mm² 7.0
(psi)
N/mm² 20.2
(psi)
N/mm² *1.2
(psi)
Technical Data Sheet
(1,010)
(2,930)
(*170)
October-2005
®

45440 Summary of contents

Page 1

... Material Safety Data Sheet (MSDS). Directions for use 1. For best performance bond surfaces should be clean and free from grease. 2. This product performs best in thin bond gaps (0.05 mm Excess adhesive can be dissolved with Loctite cleanup 60 solvents, nitromethane or acetone. 15 ≤30 LMS Loctite Material Specification LMS dated March-19, 2002 ...

Page 2

... Henkel Corporation in the U.S. and ® elsewhere. denotes a trademark registered in the U.S. Patent and Trademark Office. Reference 1.0 Henkel Loctite Americas +860.571.5100 For the most direct access to local sales and technical support visit: www.loctite.com TDS LOCTITE We cannot assume Henkel Loctite Europe +49.89.9268.0 ® ® Quicktite ...