DP-100 FR OFF-WHITE 3M, DP-100 FR OFF-WHITE Datasheet - Page 4

• Manufacturer Part Number: DP-100 FR OFF-WHITE
• Description: EPOXY 2 PART ADH, CART 1.7FL.OZ
• Manufacturer: 3M
• Series: Scotch-Weldr

Specifications of DP-100 FR OFF-WHITE

• Adhesive Type: Epoxy - 2 Part
• Color: Off White
• Weight: 1.7oz
• Volume: 50ml

3M
Epoxy Adhesive
DP-100 FR
Typical Adhesive
Performance
Characteristics
Handling/Application
Information (continued)
™
Scotch-Weld
9
Note: The following technical information and data should be considered representative
The following product performance data were obtained in the 3M laboratory under the
conditions specified. The following data show typical results obtained with the 3M™
Scotch-Weld™ Epoxy Adhesive DP-100 FR when applied to properly prepared substrates,
cured, and tested according to the specifications indicated. This data was generated using
the 3M™ EPX™ Applicator System equipped with an EPX static mixer, according to
manufacturer’s directions. Thorough manual mixing should afford comparable results.
Overlap Shear
Overlap Shear
Overlap Shear
*Time in test chamber oven before test.
Surface Preparation (continued)
Glass
1. Solvent wipe surface using acetone or methyl ethyl ketone (MEK).*
2. Apply a thin coating (0.0001 in. or less) of primer such as 3M™ Scotch-Weld™
*When using solvents, extinguish all ignition sources, including pilot lights, and
Overlap Shear (ASTM D 1002-64)
Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually
using 1" x 4" pieces of substrate except for aluminum. Two panels 0.063" thick, 4" x 7" of 2024 T-3 clad aluminum were
bonded and cut into 1" wide samples after 24 hours. The thickness of the bond line was 0.005-0.008". All strengths were
measured at 73°F (23°C) except where noted.
The separation rate of the testing jaws was 0.1" per minute for metals, 2" per minute for plastics. The thickness of the
substrates were: metals, 0.060"; plastics, 0.125".
follow manufacturer’s precautions and directions for use.
Structural Adhesive Primer EC-3901 to the glass surfaces to be bonded and allow
the primer to dry before bonding.
™
Aluminum -Etched
Cold Rolled Steel-MEK/abrade/MEK
ABS
PVC
Polycarbonate
Polyacrylic
FRP
50% RH / 25°C (77°F) 30 days
Tap Water (30 days) 23°C (73°F)
Salt Spray (30 days) 23°C (73°F)
-67°F (-55°C)
73°F (23°C)
180°F (82°C) (15 min.)*
or typical only and should not be used for specification purposes.
MEK/abrade/MEK
9
9
9
at Various Temperatures
at R.T.
After Environmental Exposure
- 4 -
2200 psi
1050 psi
1100 psi
2200 psi
2100 psi
2700 psi
1250 psi
2200 psi
800 psi
420 psi
240 psi
200 psi
145 psi
600 psi