DP-605NS OFF-WHITE 1.7 FL OZ 3M, DP-605NS OFF-WHITE 1.7 FL OZ Datasheet - Page 5

• Manufacturer Part Number: DP-605NS OFF-WHITE 1.7 FL OZ
• Description: URETHANE 2 PART ADH, CART 1.7FL.OZ
• Manufacturer: 3M
• Series: Scotch Weldr

Specifications of DP-605NS OFF-WHITE 1.7 FL OZ

• Adhesive Type: Urethane - 2 Part
• Adhesive Applications: Bonding - General Purpose
• Color: Off-White
• Dispensing Method: Dual-Cartridge
• Volume: 1.7fl.oz. (US)
• Pack Quantity: 2
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant

3M
Epoxy Adhesives
DP-100 Clear • DP-100 NS Translucent
Typical Adhesive
Performance
Characteristics
™
Scotch-Weld
Metals, Overlap Shear, Tested @ 73°F (23°C) (psi)
Note: The following product performance data was obtained in the 3M laboratory
A. Overlap Shear
B. T-peel
C. Cure Cycle
Etched Aluminum, Overlap Shear, at temperature (psi)
1
Represents time in test chamber oven before test.
Aluminum-
Cold Rolled Steel-
Stainless Steel-
Copper-
Brass-
Galvanized Steel-
Test Temp. °F (°C)
-67°F (-53°C)
73°F (23°C)
180°F (82°C) (15 min.)
Overlap shear (OLS) strengths were measured on 1 in. wide 1/2 in. overlap
specimens. These bonds were made individually using 1 in. x 4 in. pieces of
substrate except for aluminum. Two panels 0.063 in. thick, 4 in. x 7 in. of 2024 T-3
clad aluminum were bonded and cut into 1 in. wide samples after 24 hours. The
thickness of the bond line was 0.005 - 0.008 in. All strengths were measured at
73°F (23°C) except where noted. (Tests per ASTM D 1002-72.)
The separation rate of the testing jaws was 0.1 in. per minute for metals, 2 in.
per minute for plastics and 20 in. per minute for rubbers. The thickness of the
substrates were: steel, 0.060 in., other metals, 0.05-0.064 in.; rubbers, 0.125 in.;
plastics, 0.125 in.
T-peel strengths were measured on 1 in. wide bonds at 73°F (23°C). The testing
jaw separation rate was 20 inches per minute. The substrates were 0.032 in. thick.
(Tests per ASTM D 1876-61T.)
With the exception of Rate of Strength Build-Up Tests, all bonds were cured
7 days at 73°F (23°C)/50% RH before testing or subjected to further conditioning
or environmental aging.
™
under the conditions specified. The following data shows typical results obtained
with 3M™ Scotch-Weld™ Epoxy Adhesives DP-100 and DP-100 NS when applied
to properly prepared substrates, cured for 7 days at 73°F (23°C) under 2 psi cure
pressure, and tested according to the test methods indicated.
The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
Etched
MEK/abrade/MEK
MEK/abrade/MEK
MEK/abrade/MEK
MEK/abrade/MEK
MEK/abrade/MEK
MEK/abrade/MEK
1
- 5 -
DP-100 Clear
DP-100 Clear
3M™ Scotch-Weld™ Epoxy Adhesive
3M™ Scotch-Weld™ Epoxy Adhesive
1500
1500
1000
300
900
950
950
700
750
900
DP-100 NS Translucent
DP-100 NS Translucent
1500
1500
1140
1080
900
300
570
890
500
840