00101 Loctite, 00101 Datasheet - Page 6

• Manufacturer Part Number: 00101
• Description: ADHESIVE & SEALANT COMPOUND KIT
• Manufacturer: Loctite

Specifications of 00101

• Kit Contents: 242 & 262 Threadlockers, 7649 Primer/Activator, Prism 454 Instant Adhesive Gel, Quick Metal 660 Retaining Compound, 565 Thread Sealant, 587 Silicone Gasket Maker, 518 Gasket Eliminator
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant

8
* Requires heat cure to achieve temperature resistance
1. Activate inactive surfaces.
2. Speed cure times for faster return to service.
3. Speed curing through larger gaps and deep threads.
4. Substantially speed cure times on cold parts.
5. Act as a cleaning agent.
Active surfaces:
Inactive surfaces: Aluminum, stainless steel, magnesium,
Strength Required
Shear Strength
Diametrical Clearance
Temperature Resistance
Cure Time (Setup / Full Strength)
Common Sizes / Part Number
Use Loctite
Primer is optional with:
Primer is required with:
Package Size/Part Number: 1.75 oz. – 38402
Helpful Hints:
■ If the retaining compound will be applied below 40°F (5 °C),
■ All parts must be clean and dry before sealing –
■ If the parts have been in contact with washing or
Solution
pre-treat with Loctite
use Loctite
cutting fluids containing nitrites, wash with hot water
®
ODC-Free Cleaner & Degreaser
Brass, copper, bronze, iron, soft steel, nickel.
zinc, black oxide, cadmium, titanium, others.
®
Retaining
Securing Cylindrical Assemblies
■ Bond non-threaded cylindrical metal assemblies
■ High and moderate strength products – can carry high loads and eliminate fretting
■ Fill all voids – prevent corrosion
■ Reduce the need for close tolerances
■ 100 % contact – load and stress are distributed evenly over the joint
7649™ Primer N™ to:
®
7649™ Primer N™
Is the assembly badly worn?
4.5 oz. – 21348
Loctite
Quick Metal
Retaining Compound
Used for repairing worn
coaxial parts without
remachining; enables
re-use of worn bearing
seats, keys, splines, tapers,
or for retaining shims.
CFIA Approved.
Retaining Compound
Up to 0.020" (0.5 mm)
Yes - Gaps up to
0.020'' (0.5 mm)
50 ml tube – 66040
6 ml tube – 66010
20 min./24 hr.
Loctite
Quick Metal
300°F (150°C)
®
3,335 psi
660™
High
®
660™
®
®
Loctite
Retaining Compound
A controlled strength
retaining compound that is
ideal for cylindrical parts
that require disassembly.
CFIA Approved.
Up to 0.006'' (0.15 mm)
Retaining Compound
10 ml bottle – 28802
50 ml bottle – 21458
Low Strength
20 min./24 hr.
Loctite
300°F (150°C)
®
1,700 psi
641™
Low
®
641™
Loctite
Retaining Compound
– Press Fit/General
Purpose
Recommended for parts
that will need subsequent
dismantling, i.e. retention
of bearings onto shafts
and into housings.
Mil-Spec (R-46082B) Type I.
Retaining Compound
250 ml bottle – 60941
10 ml bottle – 60921
50 ml bottle – 60931
Medium Strength
Up to 0.005" (0.1 mm)
10 min./24 hr.
Loctite
300°F (150°C)
®
2,300 psi
Medium
609™
Yes
®
609™
Loctite
668™ Retaining
Compound
A high temperature
retaining compound in a
revolutionary semi-solid
formula. Patented, no-mess
package offers added
convenience and portability.
Ideal for gaps up to 0.005"
on the diameter. Withstands
temperatures to 400°F (204°C).
Retaining Compound
Up to 0.005" (0.1 mm)
19 g stick – 39148
38 g stick – 39149
QuickStix™ 668™
9 g stick – 39147
30 min./24 hr.
400°F (204°C)
Semi-Solid
®
1,870 psi
Medium
QuickStix™
Loctite
Yes to 400°F (200°C)
®
Will the parts be dismantled later for maintenance?
Loctite
Retaining Compound –
Slip Fit/High
Temperature
Recommended for high
temperature retaining of
parts with a clearance or
interference fit, i.e. retaining
bushes, bearings, seals, fans,
and liners. Requires heat
cure to achieve temperature
resistance. ABS Approved.
Retaining Compound
250 ml bottle – 62070
Up to 0.015" (0.4 mm)
10 ml bottle – 62015
50 ml bottle – 62040
30 min./24 hr.
450°F (232°C)*
e.g. bearings, sprockets, and sheeves
Loctite
®
No - Gaps to 0.015'' (0.4 mm)
3,800 psi
620™
Liquid
High
®
620™
Temperatures above 300°F (150°C )?
Loctite
Retaining Compound –
Slip Fit/High Strength
Gives best resistance to
dynamic, axial and radial
loads. Recommended for
retaining shafts, gears,
pulleys, and similar
cylindrical parts.
NSF/ANSI 61 Approved.
ABS Approved.
Retaining Compound
250 ml bottle – 68060
Up to 0.015" (0.4 mm)
10 ml bottle – 68015
50 ml bottle – 68035
2,800 psi minimum
10 min./24 hr.
Loctite
300°F (150°C)
®
680™
Oil Contamination or other?
High
No
No
®
680™
No
Loctite
Retaining Compound –
Press Fit/Oil Tolerant
For retaining close-fitting
cylindrical parts, up to
0.005" (0.1 mm) gap, and
for use on cylindrical fitting
parts where thorough
degreasing is not possible.
Applications include
retaining roller bearings or
oil impregnated bushings
into housings.
Retaining Compound
250 ml bottle – 21442
10 ml bottle – 21440
50 ml bottle – 21441
Up to 0.005" (0.1 mm)
Loctite
10 min./24 hr.
300°F (150°C)
®
3,770 psi
603™
High
Yes
®
603™
9