RN731JTTD1003B25 KOA Speer Electronics, RN731JTTD1003B25 Datasheet - Page 2
![Thin Film Resistors - SMD 1/16W 100Kohm 0.1% 25ppm](/photos/30/48/304817/rn73_l_sml.jpg)
RN731JTTD1003B25
Manufacturer Part Number
RN731JTTD1003B25
Description
Thin Film Resistors - SMD 1/16W 100Kohm 0.1% 25ppm
Manufacturer
KOA Speer Electronics
Type
Thin Filmr
Series
RN73r
Specifications of RN731JTTD1003B25
Resistance
100kohm
Package / Case
0603
Temperature Coefficient
±25
Power Rating(s)
1/16W
Tolerance (+ Or -)
0.1%
Mounting Style
Surface Mount
Operating Temp Range
-55C to 125C
Case Style
Molded
Military Standard
MIL-R-55342F
Product Length (mm)
1.6mm
Product Depth (mm)
0.8mm
Product Height (mm)
0.45mm
Tolerance
0.1 %
Power Rating
0.0625 Watt (1/16 Watt)
Voltage Rating
20 Volts
Operating Temperature Range
- 55 C to + 125 C
Termination Style
SMD/SMT
Dimensions
0.8 mm W x 1.6 mm L x 0.45 mm H
Product
Thin Film Resistors SMD
Lead Free Status / RoHS Status
Compliant
Lead Free Status / RoHS Status
Lead free / RoHS Compliant, Compliant
Available stocks
Company
Part Number
Manufacturer
Quantity
Price
Company:
Part Number:
RN731JTTD1003B25
Manufacturer:
EPCOS
Quantity:
12 000
■性能 Performance
■使用上の注意 Precautions for Use
本カタログに掲載の仕様は予告なく変更する場合があります。ご注文およびご使用前に納入仕様書で内容をご確認下さい。
車載機器、医療機器、航空機器など人命に関わったり、あるいは甚大な損害を引き起こす可能性のある機器へのご使用を検討される場合には、必ず事前にご相談下さい。
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
Contact our sales representatives before you use our products for applications including automotives, medical equipment and aerospace equipment.
Malfunction or failure of the products in such applications may cause loss of human life or serious damage.
●
●
●
●
●
●
●
●
●
●
試験項目
Test Items
抵抗値
Resistance
抵抗温度係数
T.C.R.
過負荷 (短時間)
Overload (Short time)
はんだ耐熱性
Resistance to soldering heat
温度急変
Rapid change of temperature
耐湿負荷
Moisture resistance
70℃での耐久性
Endurance at 70℃
高温放置
High temperature exposure
■負荷軽減曲線 Derating Curve
周囲温度70℃以上で使用される場合は、上図負荷軽減曲線に従って、定
格電力を軽減して御使用下さい。
For resistors operated at an ambient temperature of 70℃ or above, a power
rating shall be derated in accordance with the above derating curve.
部品のテーピング材料は適正な静電気対策を施した物を使用しておりますが、実装に際して過度な乾燥状況である場合や、テーピング包装のままで長時間振動を加えた後にはト
ップテープに製品が静電気吸着し、搭載不良を起したり、部品が静電気 (人体モデル100pF 1.5kΩにて、1J、2A、2B、2E:1kV以上 1E:0.5kV以上に相当) で破壊され抵抗値変化
を起こす危険がありますのでご注意下さい。基板実装時におきましても、同様に過度な静電気が印加されませんようご注意下さい。
本製品及び実装したプリント基板にフラックスや人の汗や唾液等に含まれるイオン性不純物質が付着しておりますと、耐湿性・耐腐食性等の点から好ましくありません。フラッ
クス内には塩素や酸、人の汗及び唾液にはナトリウムイオン (Na
ております。特に鉛フリーはんだを御使用の場合、濡れ性向上の為、イオン性物質を多く含有している事がありますので、RMA系のはんだ又はフラックスを御使用になるか、十
分な洗浄を行って下さい。また、防湿コート材を塗布される場合、製品と防湿コート間に上記汚染物が残存しますと、更に電蝕を誘発する事が確認されておりますので、防湿コ
ート材塗布前に洗浄されることをお勧めいたします。
こて先が直接製品に当たらないようご注意下さい。抵抗値変化を起こす危険性があります。また、こて先が直接保護コートに当りますと、瞬時に炭化する危険性があり、電蝕に
対する耐候性及び保護コートの絶縁性も低下しますのでご注意下さい。さらに、こて先温度が非常に高温の場合も同様に保護コートの劣化が考えられますのでご注意ください。
この製品の保管に関しましては、直射日光・高温多湿を避けて下さい。直射日光は、テーピングの変質を起し適正なピーリング強度の維持が困難となりますのでご注意下さい。5
〜35℃/35〜75%RHの場合、納入後12ヶ月間は、はんだ付け性の低下はありませんが、結露・有毒ガス (硫化水素、亜硫酸ガス、塩化水素等) ・ほこり等によりはんだ付け性が低
下致しますので保管には十分ご注意下さい。
実装したチップ抵抗器に耐熱用マスキングテープを貼り付け、剥がしますと上面電極がテープの粘着力により剥離する事があります。特に実装時の熱によりテープ粘着剤の接着
強度も高まる事も確認されております。従いまして、ご使用を控えていただきます様にお願い致します。尚、耐熱用マスキングテープをご使用される際は、テープ粘着剤が直
接、製品に触れない方法にてご対応いただけます様、ご配慮下さい。
The properly and electrostatically measured taping materials are used for the components, but attention should be paid to the fact that there is some danger the parts absorb on the
top tapes to cause a failure in the mounting and the parts are destructed by static electricity (more than 1kV : 1J, 2A, 2B, 2E
change the resistance in the conditions of an excessive dryness or after the parts are given vibration for a long time as they are packaged on the tapes. Similarly, care should be
given not to apply the excessive static electricity when mounting on the boards.
Ionic impurities such as flux etc. that are attached to these products or those mounted onto a PCB, negatively affect their moisture resistance, corrosion resistance, etc. The flux
may contain ionic substances like chlorine, acid, etc. while perspiration and saliva include ionic impurities like sodium (Na
substances may induce electrical corrosion when they invade into the products. Either thorough washing or using RMA solder and flux are necessary since lead free solder contains
ionic substances. Washing process is needed, before putting on moisture proof material in order to prevent electrical corrosion.
Please pay attention that the top of an iron does not direct touch to the components. There is a risk that may cause a change in resistance. Take care that another risk may happen
that the protecting coat is carbonized in an instant when touched directly by the top of the iron, also climatic-proof for electric corrosion or insulation of protecting coat may be
dropped down. Be sure not to give high temperature on the top of the iron as it will degrade the protecting coat.
Avoid storing components under direct sun rays, high temperature/humidity. Direct sun rays will cause quality change of taping and difficulty of keeping appropriate peeling strength. 5
〜35℃/35〜75%RH, there is no deterioration of solderability for 12 months, but take special care for storing, because condensation, dust, and toxic gas like hydrogen sulfide,
sulfurous acid gas, hydrogen chloride, etc. may drop solderability.
The upper electrodes could be peeled off when a heat-resistant masking tape is attached to the mounted chip resistors and then detached from them. It is confirmed that the
adhesiveness gets stronger due to the exposure to heat under mounting. Accordingly, we recommend the use of masking tape be refrained. If the use of heat-resistant masking tape is
unavoidable, please make sure that the adhesives on the tape do not directly come in contact with the product.
100
80
60
40
20
0
-60 -40 -20
-55
周囲温度 Ambient temperature (℃)
0
規格値 Performance Requirements
ΔR± (%+0.05Ω)
保証値 Limit
規定の許容差内
Within specified tolerance
規定値内
Within specified T.C.R.
0.1
0.1
0.25
0.5
0.25
0.25
20 40 60
70
80 100120 140
+
)、塩素イオン (Cl
125
代表値 Typical
—
—
0.01
0.04
0.03
0.06
0.02
0.01
−
) 等が含まれておりますので、製品がそれらに汚染されると電蝕が誘発される事が確認され
試験方法
Test Methods
25℃
+25℃/ +125℃:T.C.R.=±5 (×1 0
+25℃/ −55℃ and +25℃ / +125℃:another
定格電圧 × 2.5 倍又は最高過負荷電圧の低い方を 5 秒印加
Rated voltage × 2.5 or Max. overload vol., whichever is less, for 5s
260℃±5℃, 10s±1s
−55℃ (30min.) /+125℃ (30min.) 5 cycles
40℃±2℃, 90%〜95%RH, 1000h
1.5時間 ON / 0.5時間 OFFの周期 1.5h ON / 0.5h OFF cycle
70℃±2℃, 1000h
1.5時間 ON / 0.5時間 OFFの周期 1.5h ON / 0.5h OFF cycle
+125℃, 100h
あ1
あ1
+
), chlorine (Cl
0.5kV : 1E, Human Body Model 100pF 1.5kΩ) to
−
) etc. Therefore these kinds of ionic
−6
/ K)
www.koanet.co.jp