GNM314R72A331KD01D Murata Electronics North America, GNM314R72A331KD01D Datasheet - Page 51
![CAP 4-ARRAY 330PF 100V X7R 1206](/photos/0/92/9281/4-array_series_1206_sml.jpg)
GNM314R72A331KD01D
Manufacturer Part Number
GNM314R72A331KD01D
Description
CAP 4-ARRAY 330PF 100V X7R 1206
Manufacturer
Murata Electronics North America
Series
GNMr
Datasheet
1.GNM212R61A225MA01D.pdf
(151 pages)
Specifications of GNM314R72A331KD01D
Capacitance
330pF
Voltage - Rated
100V
Dielectric Material
Ceramic
Number Of Capacitors
4
Circuit Type
Isolated
Temperature Coefficient
X7R
Tolerance
±10%
Mounting Type
Surface Mount
Package / Case
1206 (3216 Metric)
Height
0.031" (0.80mm)
Size / Dimension
0.126" L x 0.063" W (3.20mm x 1.60mm)
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Other names
490-3417-2
!Note
• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
sales representatives or product engineers before ordering.
!Note
No.
12
13
14
15
16
17
18
Continued from the preceding page.
Resistance
to Soldering
Heat
Deflection
Solderability of
Termination
Temperature
Cycle
Humidity,
Steady
State
Humidity
Load
High
Temperature
Load
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
Item
Appearance
Capacitance
Change
D.F.
I.R.
Dielectric
Strength
Appearance
Capacitance
Change
D.F.
I.R.
Dielectric
Strength
Appearance
Capacitance
Change
D.F.
I.R.
Dielectric
Strength
Appearance
Capacitance
Change
D.F.
I.R.
Appearance
Capacitance
Change
D.F.
I.R.
No cracking or marking defects should occur.
75% of the terminations are to be soldered evenly and
continuously.
No defects or abnormalities
Within T7.5%
0.01 max.
More than 10,000MΩ
No failure
No defects or abnormalities
Within T7.5%
0.01 max.
More than 10,000MΩ
No failure
No defects or abnormalities
Within T12.5%
0.02 max.
More than 1,000MΩ
No failure
No defects or abnormalities
Within T12.5%
0.02 max.
More than 500MΩ
No defects or abnormalities
Within T12.5%
0.02 max.
More than 1,000MΩ
GRM21
Type
Specifications
1.2
a
100
Fig. 2
b
c
a
4.0
b
4.5
t : 1.6mm
1.65
c
(in mm)
Solder the capacitor to the test jig (glass epoxy boards) shown
in Fig. 2 using a eutectic solder.
Then apply a force in the direction shown in Fig. 3.
The soldering should be done by the reflow method and should
be conducted with care so that the soldering is uniform and free
of defects such as heat shock.
Immerse the capacitor in a solution of ethanol (JIS-K-8101) and
rosin (JIS-K-5902) (25% rosin in weight proportion). Preheat at
80 to 120D for 10 to 30 seconds. After preheating, immerse in
eutectic solder solution for 2T0.5 seconds at 230T5D or
Sn-3.0Ag-0.5Cu solder solution for 2T0.5 seconds at 245T5°C.
Preheat the capacitor at 120 to 150D for 1 minute. Immerse the
capacitor in a eutectic solder or Sn-3.0Ag-0.5Cu solder solution
at 270T5D for 10T0.5 seconds. Let sit at room temperature for
24T2 hours, then measure.
Fix the capacitor to the supporting jig in the same manner and
under the same conditions as (11).
Perform the five cycles according to the four heat treatments
listed in the following table. Let sit for 24T2 hours at room tem-
perature, then measure.
Sit the capacitor at 40T2D and 90 to 95% humidity for 500T12
hours.
Remove and let sit for 24T2 hours at room temperature, then
measure.
Apply the rated voltage at 40T2D and 90 to 95% humidity for
500T12 hours. Remove and let sit for 24T2 hours at room tem-
perature, then measure. The charge/discharge current is less
than 50mA.
Apply 200% of the rated voltage for 1,000T12 hours at 85T3D.
Let sit for 24T2 hours at room temperature, then measure.
The charge/discharge current is less than 50mA.
Specifications and Test Methods
Temp. (D)
Time (min.)
Step
Y25
30T3
R230
1
Capacitance meter
45
W0
Y3
Fig.3
Test Method
20
Room Temp.
2 to 3
50
2
Pressurize
45
Pressurizing
speed : 1.0mm/sec.
Flexure : V1
85
30T3
3
W3
Y0
(in mm)
Room Temp.
2 to 3
4
C02E.pdf
49
07.2.6
8