C1206C100J5GACTU Kemet, C1206C100J5GACTU Datasheet - Page 9
![CAP CERAMIC 10PF 50V NP0 1206](/photos/10/53/105350/1206_kemet_mlcc_caps_sml.jpg)
C1206C100J5GACTU
Manufacturer Part Number
C1206C100J5GACTU
Description
CAP CERAMIC 10PF 50V NP0 1206
Manufacturer
Kemet
Series
C1206r
Specifications of C1206C100J5GACTU
Capacitance
10pF
Voltage - Rated
50V
Tolerance
±5%
Temperature Coefficient
C0G, NP0
Mounting Type
Surface Mount, MLCC
Operating Temperature
-55°C ~ 125°C
Applications
General Purpose
Package / Case
1206 (3216 Metric)
Size / Dimension
0.126" L x 0.063" W (3.20mm x 1.60mm)
Thickness
0.78mm
Voltage Rating
50 Volts
Operating Temperature Range
- 55 C to + 125 C
Temperature Coefficient / Code
C0G (NP0)
Product
General Type MLCCs
Dimensions
1.6 mm W x 3.2 mm L x 1.5 mm H
Dissipation Factor Df
0.1
Termination Style
SMD/SMT
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Features
-
Ratings
-
Lead Spacing
-
Lead Free Status / Rohs Status
Lead free / RoHS Compliant
Other names
399-1192-2
C1206C100J5GAC
C1206C100J5GAC7800
C1206C100J5GAC
C1206C100J5GAC7800
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – C0G Dielectric, 10VDC-200VDC (Commercial Grade)
Soldering Process
Recommended Soldering Technique:
Recommended Soldering Profile:
Table 4 – Performance & Reliability: Test Methods and Conditions
Storage and Handling
Ceramic chip capacitors should be stored in normal working environments. While the chips themselves are quite robust in other
environments, solderability will be degraded by exposure to high temperatures, high humidity, corrosive atmospheres, and long term
storage. In addition, packaging materials will be degraded by high temperature – reels may soften or warp, and tape peel force may
increase. KEMET recommends that maximum storage temperature not exceed 40ºC, and maximum storage humidity not exceed
70% relative humidity. In addition, temperature fluctuations should be minimized to avoid condensation on the parts, and atmospheres
should be free of chlorine and sulfur bearing compounds. For optimized solderability, chip stock should be used promptly, preferably
within 1.5 years of receipt.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
• Solder wave or solder reflow for EIA case sizes 0603, 0805 and 1206
• All other EIA case sizes are limited to solder reflow only
• KEMET recommends following the guidelines outlined in IPC/JEDEC J-STD-020
Resistance to Solvents
High Temperature Life
Temperature Cycling
Moisture Resistance
Mechanical Shock
Terminal Strength
Biased Humidity
Thermal Shock
Solderability
Storage Life
Board Flex
Stress
MIL-STD-202 Method 103
MIL-STD-202 Method 106
MIL-STD-202 Method 107
MIL-STD-202 Method 108
MIL-STD-202 Method 108
MIL-STD-202 Method 213
MIL-STD-202 Method 215
JESD22 Method JA-104
Reference
JIS-C-6429
JIS-C-6429
J-STD-002
/ EIA -198
Appendix 1, Note: Force of 1.8kg for 60 seconds.
Appendix 2, Note: 2mm (min) for all except 3mm for C0G.
Magnification 50 X. Conditions:
1000 Cycles (-55°C to +125°C), Measurement at 24 hours. +/- 2 hours after test conclusion.
Load Humidity: 1000 hours 85°C/85%RH and Rated Voltage. Add 100K ohm resistor. Measurement
at 24 hours. +/- 2 hours after test conclusion.
Low Volt Humidity: 1000 hours 85°C/85%RH and 1.5V. Add 100K ohm resistor.
Measurement at 24 hours. +/- 2 hours after test conclusion.
t = 24 hours/cycle. Steps 7a & 7b not required. Unpowered.
Measurement at 24 hours. +/- 2 hours after test conclusion.
-55°C/+125°C. Note: Number of cycles required-300, Maximum transfer time-20 seconds, Dwell
time-15 minutes. Air-Air.
1000 hours at 125°C (85°C for X5R, Z5U and Y5V) with 2 X rated voltage applied.
150°C, 0VDC, for 1000 Hours.
Figure 1 of Method 213, Condition F.
Add aqueous wash chemical - OKEM Clean or equivalent.
a) Method B, 4 hours @ 155°C, dry heat @ 235°C
b) Method B @ 215°C category 3
c) Method D, category 3 @ 260°C
Test or Inspection Method
C1003_C0G • 5/27/2011
9