F9469PC 3/8"X60YD 3M, F9469PC 3/8"X60YD Datasheet - Page 3

• Manufacturer Part Number: F9469PC 3/8"X60YD
• Description: TRANSFER TAPE 9469PC 3/8" X 60YD
• Manufacturer: 3M
• Series: VHB™r

Specifications of F9469PC 3/8"X60YD

• Tape Type: Adhesive Transfer Tape
• Adhesive: Acrylic, 100MP
• Backing, Carrier: Polycoated Kraft Liner
• Thickness: 0.0090" (9.0 mils, 0.229mm)
• Thickness - Adhesive: 0.0050" (5.0 mils, 0.127mm)
• Thickness - Backing, Carrier, Liner: 0.0040" (4.0 mils, 0.102mm)
• Width: 0.38" (9.65mm) 3/8"
• Length: 180' (55.0m) 60 yds
• Color: Clear
• Usage: Attachment, High Temperature Applications
• Temperature Range: 300°F (149°C)
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Other names: 00-021200-42910-1; 3M9039; 70-0062-7763-9

3M
F9460PC • F9469PC • F9473PC
Weight Loss and
Outgassing
Performance
UL 746C Listings
(File MH 17478) and
Durability Testing
™
VHB
™
Adhesive Transfer Tapes with Adhesive 100MP
3M™ Adhesive 100MP has UL 746C listings with different temperature ratings on many
commonly used substrate materials as indicated in the table below. Qualification for this
listing requires high strength retention after extended exposure to high temperatures,
humidity, cold, and cyclic conditions.
Substrates
Stainless Steel, Glass/Epoxy, Enameled Steel, Ceramic, Phenolic;
Nickel Plated Steel (3M™ Adhesive Transfer Tape F9469PC only)
ABS, Polycarbonate, Aluminum, Galvanized Steel
Unplasticized PVC
Our testing has shown that 3M adhesive 100MP yielded 92% retention of peel adhesion
after the roll was aged for more than 5 years at an elevated temperature of 150°F (65°C).
The initial tack and liner release properties were still excellent. This testing result suggests
that the tape is relatively unaffected by long-term exposure to elevated temperatures. Bonds
made with 3M adhesive 100MP can tolerate periodic short-term exposures to temperatures
up to 500°F (260°C).
3M adhesive 100MP is thermoplastic
in nature, becoming softer as
temperature increases and firmer as
temperature decreases. As the
adhesive becomes firmer, the
performance generally increases.
This performance increase is
demonstrated graphically in Figure 1
for 3M™ VHB™ Adhesive Transfer
Tape F9473PC. It shows the
breakaway and peel forces as
a function of temperature. The
exception of the performance
increase is at very low temperatures
when high impact stresses along with high frequencies are encountered. At low temperatures,
the tape becomes very firm and glassy; the ability to absorb impact energy is reduced.
The testing was done per ASTM E595-77/84/90 as indicated in the NASA Reference
Publication 1124, Revision 4, “Outgassing Data for Selecting Spacecraft Materials”,
June 1997. The results are reported as percentage of total mass loss (TML) and
percentage of Volatile Condensible Materials (VCM), respectively, as shown below.
Products
TML (%)
VCM (%)
Note: The following technical information and data should be considered representative or
typical only, and should not be used for specification purposes.
F9460PC
3M™ VHB™ Adhesive Transfer Tapes
0.85
0.00
F9469PC
1.29
0.02
- 3 -
F9473PC
100
90
80
70
60
50
40
30
20
10
0
(3M™ VHB™ Adhesive Transfer Tape F9473PC on Aluminum)
1.23
0.01
-65
Figure 1. T-Peel Performance vs. Temperature
-20
Temperature °F
0
Temperature Rating
110°C
90°C
75°C
20
Break Away
Peel
70