06035C104KAT2A AVX Corporation, 06035C104KAT2A Datasheet - Page 2

• Manufacturer Part Number: 06035C104KAT2A
• Description: CAP CER .10UF 50V X7R 10% 0603
• Manufacturer: AVX Corporation

Specifications of 06035C104KAT2A

• Capacitance: 0.1µF
• Tolerance: ±10%
• Package / Case: 0603 (1608 Metric)
• Voltage - Rated: 50V
• Temperature Coefficient: X7R
• Mounting Type: Surface Mount, MLCC
• Operating Temperature: -55°C ~ 125°C
• Applications: General Purpose
• Size / Dimension: 0.063" L x 0.031" W (1.60mm x 0.80mm)
• Thickness: 0.90mm Max
• Voltage Rating: 50 Volts
• Operating Temperature Range: - 55 C to + 125 C
• Temperature Coefficient / Code: X7R
• Product: General Type MLCCs
• Dimensions: 0.81 mm W x 1.6 mm L
• Dissipation Factor Df: 10
• Termination Style: SMD/SMT
• Dielectric Characteristic: X7R
• Capacitance Tolerance: ± 10%
• Capacitor Case Style: 0603
• No. Of Pins: 2
• Capacitor Mounting: SMD
• Rohs Compliant: Yes
• Case Size: 0603
• Material, Element: Ceramic
• Termination: SMT
• Voltage, Rating: 50 VDC
• Lead Free Status / RoHS Status: Lead free / RoHS Compliant
• Features: -
• Ratings: -
• Lead Spacing: -
• Lead Free Status / Rohs Status: Lead free / RoHS Compliant
• Other names: 06035C104KAT2A; 478-5052-2

X7R Dielectric
Specifications and Test Methods
Resistance to
Resistance to
Operating Temperature Range
Solder Heat
Load Life
Humidity
Stresses
Thermal
Flexure
Shock
Load
Insulation Resistance
Dielectric Strength
Dissipation Factor
Parameter/Test
Capacitance
Solderability
Capacitance
Capacitance
Capacitance
Capacitance
Capacitance
Appearance
Appearance
Appearance
Appearance
Appearance
Resistance
Resistance
Resistance
Resistance
Resistance
Dissipation
Dissipation
Dissipation
Dissipation
Dissipation
Insulation
Insulation
Insulation
Insulation
Insulation
Dielectric
Dielectric
Dielectric
Dielectric
Variation
Variation
Strength
Variation
Strength
Variation
Strength
Variation
Strength
Factor
Factor
Factor
Factor
Factor
No defects, <25% leaching of either end terminal
≥ 95% of each terminal should be covered
No breakdown or visual defects
≥ Initial Value x 0.3 (See Above)
≥ Initial Value x 0.3 (See Above)
Meets Initial Values (As Above)
Meets Initial Values (As Above)
Meets Initial Values (As Above)
Meets Initial Values (As Above)
≤ Initial Value x 2.0 (See Above)
Meets Initial Values (As Above)
≤ Initial Value x 2.0 (See Above)
Meets Initial Values (As Above)
100,000MΩ or 1000MΩ - µF,
Meets Initial Values (As Above)
Meets Initial Values (As Above)
Meets Initial Values (As Above)
X7R Specification Limits
≤ 2.5% for ≥ 50V DC rating
≤ 5.0% for ≤ 10V DC rating
Within specified tolerance
≤ 3.0% for 25V DC rating
≤ 3.5% for 16V DC rating
≥ Initial Value x 0.3
No visual defects
-55ºC to +125ºC
whichever is less
with fresh solder
No visual defects
No visual defects
No defects
≤ ±12.5%
≤ ±12.5%
≤ ±12%
≤ ±7.5%
≤ ±7.5%
1-5 seconds, w/charge and discharge current
Charge device with 300% of rated voltage for
seconds. Store at room temperature for 24 ± 2
hours before measuring electrical properties.
Dip device in eutectic solder at 260ºC for 60
Step 1: -55ºC ± 2º
Step 2: Room Temp
Step 3: +125ºC ± 2º
Step 4: Room Temp
Repeat for 5 cycles and measure after
24 ± 2 hours at room temperature
Dip device in eutectic solder at 230 ± 5ºC
85% ± 5% relative humidity for 1000 hours
Store in a test chamber set at 85ºC ± 2ºC/
Note: Charge device with 150% of rated
Charge device with twice rated voltage in
Remove from test chamber and stabilize
Remove from chamber and stabilize at
120 ± 5 secs @ room temp/humidity
For Cap > 10 µF, 0.5Vrms @ 120Hz
Charge device with rated voltage for
at room temperature for 24 ± 2 hours
(+48, -0) with rated voltage applied.
room temperature and humidity for
test chamber set at 125ºC ± 2ºC
24 ± 2 hours before measuring.
Temperature Cycle Chamber
voltage for 500V devices.
Measuring Conditions
Voltage: 1.0Vrms ± .2V
for 1000 hours (+48, -0)
Test Time: 30 seconds
limited to 50 mA (max)
Freq.: 1.0 kHz ± 10%
for 5.0 ± 0.5 seconds
before measuring.
Deflection: 2mm
90 mm
1mm/sec
30 ± 3 minutes
≤ 3 minutes
30 ± 3 minutes
≤ 3 minutes
13