LMK107B7105MA-T Taiyo Yuden, LMK107B7105MA-T Datasheet - Page 33
![CAP CERM 1.0UF 10V X7R 0603](/photos/10/51/105162/emk_gmk_jmk_lmk_tmk_umk_series_0603_sml.jpg)
LMK107B7105MA-T
Manufacturer Part Number
LMK107B7105MA-T
Description
CAP CERM 1.0UF 10V X7R 0603
Manufacturer
Taiyo Yuden
Series
LMKr
Datasheet
1.LMK105BJ104KV-M.pdf
(51 pages)
Specifications of LMK107B7105MA-T
Package / Case
0603 (1608 Metric)
Mounting Type
Surface Mount, MLCC
Operating Temperature
-55°C ~ 125°C
Temperature Coefficient
X7R
Size / Dimension
0.063" L x 0.032" W (1.60mm x 0.80mm)
Applications
General Purpose
Tolerance
±20%
Capacitance
1.0µF
Thickness
0.80mm
Dielectric Characteristic
X7R
Capacitance Tolerance
± 20%
Voltage Rating
10VDC
Capacitor Case Style
0603
No. Of Pins
2
Capacitor Mounting
SMD
Rohs Compliant
Yes
Lead Free Status / RoHS Status
Lead free / RoHS Compliant
Features
-
Ratings
-
Lead Spacing
-
Other names
CE LMK107 B7105MA-T::LMK107BJ105MA-T::LMK107BJ105MA-T
【Test Methods and Remarks】
【Test Methods and Remarks】
【Test Methods and Remarks】
【Test Methods and Remarks】
【Test Methods and Remarks】
■
* This catalog contains the typical specification only due to the limitation of space. When you consider the purchase of our products, please check our specification.
mlcc06_reli_e-01
12. Resistance to Soldering
Specified Value
13. Temperature Cycle ( Thermal Shock)
Specified Value
Preconditioning:Thermal treatment (at 150℃ for 1hr) Note1
Conditions for 1 cycle/ Step 1: Minimum operating temperature
14. Humidity ( Steady state)
Specified Value
15. Humidity Loading
Specified Value
16. High Temperature Loading
Specified Value
Note1
Note2
Note3
Preconditioning:Thermal treatment (at 150℃ for 1hr) Note1
Solder temperature:270±5℃
Duration:3±0.5sec.
Preheating conditions: 80 to 100℃, 2 to 5 min.
Recovery : 24±2hrs under the standard condition
Number of cycles:5 times
Recovery : 24±2hrs under the standard condition
Preconditioning:Thermal treatment (at 150℃ for 1hr) Note1
Temperature:40±2℃
Humidity:90 to 95%RH
Duration: 500
Recovery : 24±2hrs under the standard condition
According to JIS 5102 clause 9.9.
Preconditioning:Voltage treatment
Temperature:40±2℃
Humidity:90 to 95%RH
Applied voltage:Rated voltage
Charge/discharge current:50mA max.
Duration: 500
Recovery : 24±2hrs under the standard condition
According to JIS 5102 clause 9.10.
Preconditioning:Voltage treatment
Temperature:125±3℃ (B7, C7) , 85±2℃ (BJ)
Applied voltage:Rated voltage×2 ( HMK)
Charge/discharge current:50mA max.
Duration: 1000
Recovery : 24±2hrs under the standard condition
For details of each product (characteristics graph, reliability information, precautions for use, and so on), see our Web site (http://www.ty-top.com/) or CD catalogs.
RELIABILITY DATA
Thermal treatment : Initial value shall be measured after test sample is heat-treated at 150+0/-10℃ for an hour and kept at room temperature for 24±2hours.
Voltage treatment : Initial value shall be measured after test sample is voltage-treated for an hour at both the temperature and voltage specified in the test conditions, and
Standard condition: Temperature: 5 to 35℃, Relative humidity: 45 to 85 % RH, Air pressure: 86 to 106kPa
+24
-0
+24
-0
+24
-0
Rated voltage×1.5 ( QMK)
Rated voltage×1.2 ( SMK)
hrs
hrs
hrs
150 to 200℃, 2 to 5min.
Step 2: Normal temperature
Step 3: Maximum operating temperature
Step 4: Normal temperature
kept at room temperature for 24±2hours.
When there are questions concerning measurement results, in order to provide correlation data, the test shall be conducted under the following condi-
tion.
Temperature: 20±2℃,
Unless otherwise specified, all the tests are conducted under the "standard condition".
Note2
Note2
Note3
Note3
Note3
Note3
Note3
Relative humidity: 60 to 70 % RH, Air pressure: 86 to 106kPa
Appearance:
Capacitance change:
Dissipation factor :
Insulation resistance:
Withstanding voltage ( between terminals) : No abnormality
Appearance:
Capacitance change: Within±15% (HMK) , ±7.5% (QMK, SMK)
Dissipation factor:
Insulation resistance: Initial value
Appearance:
Capacitance change: Within±15%
Dissipation factor :
Insulation resistance: 25MΩ μF or 1000MΩ, whichever is smaller.
Appearance:
Capacitance change: Within±15%
Dissipation factor:
Insulation resistance: 10MΩ μF or 500MΩ, whichever is smaller.
Appearance:
Capacitance change: Within±15%
Dissipation factor:
Insulation resistance: 50MΩ μF or 1000MΩ, whichever is smaller.
+0
-3
+0
-3
℃ 30±3min.
℃ 30±3min.
2 to 3min.
2 to 3min.
No abnormality
7%max ( HMK) , 5%max ( QMK, SMK) .
No abnormality
Initial value
No abnormality
7%max ( HMK) , 5%max ( QMK, SMK) .
No abnormality
7%max ( HMK) , 5%max ( QMK, SMK) .
1 1
No abnormality
Within±15% (HMK) , ±10% (QMK, SMK)
Initial value
Initial value
mlcc06_reli-R2